PCB Prototype and Turnkey PCB Assembly

Your Best PCB & PCB Assembly Supplier

PCB Blog
Future Trends of Flexible Circuit Boards
Rigid-Flex PCB Stack-up for Impedance Controlled Designs
Control Impedance Between Rigid PCB and Flex PCB
Flex PCB Reliability and Bendability
Normal Flex PCB Specifications
Flex PCB Polyimide Coverlay and Solder Mask
Flex PCB Boards and Connectors
About RA Copper and ED Copper
Introduction of Flexible PCB
5 Tips For Designing Flexible PCB
Advantages of FPC (Flexible PCB)
Evolution of the Flex Printed Circuit Board
Benefits of Using Flex Circuit Boards
Why Rigid-Flex PCBs are Economical?
Flexible PCB vs Rigid PCB
Development of Flexible printed circuit board (FPC) market
Traditional Manufacture Engineering of FPC Substrate
Development Trend of FPC Board
Flex PCB and the Manufacturing
About Flex PCB design
About Flex PCB and Assembly
How to Ensure Flex PCB Design Success
How to Select the Appropriate FPC Materials?
The Differences In Rigid PCB, Flex PCB and Rigid-Flex PCB
Flex-Rigid PCB Design Guidelines
Beneficials for Polyimide Flex PCB Boards
About Stiffener on Flex PCB FPC circuit Boards
About ENIG and ENEPIG
PCB Surface Finish Comparison
Copper Thickness for FPC Boards
Interconnect Solutions for Flexible Printed Circuits and Etched Foil Heaters
Advantages and Disadvantages of Rigid-Flex PCB
About FPC Plating Process
About EMI shield design for Flex Printed Circuit Board
PCB Assembly Blog
About PCB Assembly
QFP and BGA and the Development Trend in PCB assembly
Why some components need be baked before reflow soldering
About Flex PCB Assembly
Manual Soldering in SMT Assembly Manufacturing Process
BGA Components and BGA Assembly
Quick Understanding for PCB Assembly Process
About SMT Assembly (Surface Mount Technology)
About THT Assembly (Through-Hole Technology)
About Reflow Soldering
About_Wave_Soldering
PCB Assembly Inspections and Tests
Panel Requirements for PCB Assembly
About SMT (Surface Mount Technology)

Wave soldering is a process by which large printed circuit boards can be soldered quickly and reliably during PCB assembly and normally used for THT parts assembly.

 

The wave soldering process gains its name from the fact that the process passes the printed circuit boards to be soldered over a wave of solder.

 

In this way a complete board can be soldered in a matter of seconds producing joints that are reliably, both mechanically and electrically. Apart from being much faster than manual soldering, wave soldering is also produces joints with a much higher degree of reliability.

 

Wave soldering can be used in PCB assembly for both conventional through hole mounted components as well as surface mount components. However other methods such as infra-red reflow soldering are more applicable to the fine features being used today on printed circuit boards for surface mount components.

 

Wave soldering machine


The wave soldering machine consists of a heated tank of solder. This is maintained at the required temperature for the soldering process. Within the tank, a wave of solder is set up and the printed circuit boards are passed over this so that the underside of the board just contacts the solder wave. Care must be taken in adjusting the height of the wave so that it does not flow over the top side of the board where it would cause solder to enter places where it is not required.

 

The boards are held firmly in place on a conveyor using metal fingers. These are typically made of titanium because it is able to withstand the temperatures and it is not affected by the solder.

 

Preparation


In order that a electronics printed circuit board may be successfully processing using a wave soldering machine, it is necessary that it is designed and manufactured in the correct manner.

 

Solder resist layer:   The first is standard practice when designing boards these days. A solder resist or solder mask layer is included in the PCB design, and this adds a layer of "varnish" like material to the board to which the solder will not adhere. Only those areas where the solder is required are left exposed. This solder resist is most commonly green on colour.


Pad spacing:   The second main precaution is to ensure that there is sufficient spacing between the solder pads requiring soldering. If they are too close then there is the possibility that the solder may bridge the two pads causing a short circuit.

 

In view of the way that wave soldering works, where the solder wave is caused by the solder flowing out of the reservoir tank, and the board passes over it, the spacing requirements are dependent upon the direction of the board relative to the solder flow. Pads that are spaced apart in the direction of the solder flow should have a greater spacing than those that are spaced at right angles to the solder flow. This is because it is much easier for solder bridges to occur in the direction of the solder flow.

 

Fluxing


To ensure that the areas to be soldered are clean and free from oxidation, etc, flux is required. Flux is applied to the side of the board to be soldered, i.e. the underside. Careful control of the quantities of flux are needed. Too little flux and there is a high risk of poor joints, and too much flux and there will be residual flux on the board. While this does not look good cosmetically, there is also the risk of long term degradation because of the acidic nature of the flux.. There are two main methods of applying the flux::

 

Spray flux;   A fine mist of flux is sprayed ontoth e underside of the board that is to be soldered. Some systems may even use a compressed air jet to remove the excess flux.


Foam flux;   The electronic printed circuit board is passed over a cascading head of flux foam. This is generated using a tank of flux into which a plastic cylinder with tiny holes is immersed. The plastic cylinder is covered with a metal chimney and air is forced through the cylinder. This causes flux foam to rise up the chimney.

 

Preheat


The wave soldering process exposes the electronic printed circuit boards to considerable levels of heat, far greater than those it would be subjected to if it were to be manually soldered. This thermal shock would give rise to a considerably increased level of failure if it were not addressed. To overcome this the board is preheated so that it can be steadily brought up to the required temperature steadily so that any thermal shock is minimised.

 

The preheating area normally uses hot air heaters that blow hot air onto the boards as they pass towards the wave soldering machine. On some occasions, particularly if the board is densely populated, infra-red heaters may be used as well. This ensures that all the board is evenly heated and no shadow areas are present.

 

While the pre-heating is required to prevent the thermal shock that the wave soldering machine would generate, the heating is also necessary to activate the flux. This flux is required to ensure that the areas to be soldered are clean and will take the solder.

 

Applications of wave soldering


Wave soldering is not as widely used for PCB assembly as it was at one time. It is not suited to the very fine pitches required by many of the boards in manufacture today. However it is ideal for the many boards still manufactured with conventional leaded components and some surface mount boards that use larger components.

Contact us

  • Email: sales@semipcb.com
  • Tel: 086 18576671093
  • Skype: Downey.Jin_PCB&PCBA
  • Address: No.12, Shapuwei Industrial Road
  • Baoan District, Shenzhen, China

About us

  • Based in Shenzhen China, SemiPCB is professional at PCB
    and PCB Assembly for Rigid PCB, Flex PCB, Rigid-flex PCB.
  • PCB compliant ISO9001, ISO14001, TS16949, UL, RoHS.
    PCB Assembly compliant ISO9001, IATF16949, IPC-A-610E.
  • Our aim is to "become the best supplier for PCB prototype
    and Turnkey PCB Assembly".

Certifications

© 2023~2033 SemiPCB All Rights Reserved